LT MODEL GRAY RESIN

• Offering superb dimensional stability
• Suitable thermoforming for orthodontic models
• MMA free organic chemistry formulation, not smelly
• Produced under ISO standards 13485:2016
• Find here validated DLP, LCD 3D printer list

Material PropertiesValueStandardTensile strength26.2 MpaASTM D638Flexural strength99 MpaASTM D790-02Flexural modulus2640 MpaASTM D790-02Shore Hardness76.75 DASTM D2240Density1.1 g/cm3 at 23 CASTM D1475Viscosity200-225 mPa.s at 23 CDIN 53211-4ColorLight Pink

1- Washing

After the printing is completed, wash the part as attached to the building plate with ethyl alcohol (>%90) or isopropyl alcohol (>%90) for 5 minutes. Make sure that alcohol covers the part entirely when washing. Use a brush to remove uncured resin if needed. Do not over-wash, it may cause deterioration in dimensions of the part.

2- Drying

Use air-compressor to dry the washed part. Make sure that the part is dry and uncured resin is cleaned up completely. If still uncured resin left on the part, wash it with fresh alcohol and dry again.

3- Part Removal

Remove the printed part from the building plate using a scraping tool. Be very careful not to damage the model.

4- Post Curing

You can reach 99 MPa flexural strength after curing Please cure 20 minutes with MEDIFIVE curing chamber at 3rd-degree light intensity Otoflash curing recommendations; 10000 flashes without gas. After post curing, supports should be removed from the model cautiously.

Store the PowerResins Model bottle in dark and moisture free place at room temperature (20-24 °C).

Do not forget shaking the resin well before use.

If your printer has heater, you can set the temperature at 32 °C. Otherwise, you can heat your resin in a microwave for 18 seconds or by submerging in hot water for 15-20 minutes.